Production technology of zinc aluminum magnesium photovoltaic bracket production equipment

Production technology of zinc aluminum magnesium photovoltaic bracket production equipment

First, let’s introduce the automatic repair of zinc, aluminum and magnesium.

Automatic repair, zinc, aluminum and magnesium will automatically repair coatings on cuts, stampings and profiles;

The reason is that the coating undergoes a chemical reaction in the air. Magnesium ions first form magnesium hydroxide, and then the magnesium hydroxide absorbs carbon dioxide to form magnesium carbonate. This substance has a buffering effect on the PH value and reduces the dissolution rate of zinc in water. anode area and inhibit oxidation.

The formation of zinc and magnesium promotes the formation of dense corrosion products and reduces the diffusion rate of dissolved oxygen, thereby reducing the oxygen reduction rate in the cathode region. Among them, magnesium ions and oxygen ions undergo a redox reaction, and the "white rust" protective layer formed on the bracket realizes automatic repair.

Therefore, in the case of cutting, punching and cross-sections that damage the coating, the magnesium ion redox reaction will migrate to the damaged part of the coating to form a dense magnesium carbonate protective film, and the density will not be fatal! Thus achieving automatic repair.

Corrosion resistance, the corrosion resistance of zinc, aluminum and magnesium is 5-10 times that of traditional hot-dip galvanizing;

Traditional hot-dip galvanizing coatings have many coatings, and red rust will occur on the exposed parts in the early stages of corrosion. As the corrosion time prolongs, the area of red rust will increase; the film "white rust" is a dense protective layer formed on the bracket, which can achieve self-repair.

Therefore, compared with traditional products, zinc, aluminum and magnesium coatings can achieve better corrosion resistance and less coating adhesion, thus saving material and time. It has better protection for the cutting edge of the steel plate, the welded part and the parts where the coating is damaged due to severe deformation.

Production process of zinc aluminum magnesium photovoltaic bracket

Aluminum magnesium zinc material---photovoltaic bracket production line----finished product packaging---loading and delivery

Unloading rack --- Leveling machine -- Servo feeder -- Automatic punch punching --- Forming host continuous forming -- Cutting to length